Selective leaching of a mixed nickel-cobalt hydroxide precipitate in sulphuric acid solution with potassium permanganate as oxidant

Hussaini S., Ichlas Z. T., TOP S., KURŞUNOĞLU S., Kaya M.

Separation Science and Technology (Philadelphia), vol.56, pp.2475-2484, 2021 (SCI-Expanded) identifier identifier

  • Publication Type: Article / Article
  • Volume: 56
  • Publication Date: 2021
  • Doi Number: 10.1080/01496395.2020.1832523
  • Journal Name: Separation Science and Technology (Philadelphia)
  • Journal Indexes: Science Citation Index Expanded (SCI-EXPANDED), Scopus, Academic Search Premier, Aerospace Database, Analytical Abstracts, Applied Science & Technology Source, Biotechnology Research Abstracts, Chemical Abstracts Core, Chimica, Communication Abstracts, Compendex, INSPEC, Metadex, Pollution Abstracts, DIALNET, Civil Engineering Abstracts
  • Page Numbers: pp.2475-2484
  • Keywords: Selective leaching, potassium permanganate, mixed nickel-cobalt hydroxide precipitate, solvent extraction, nickel
  • Abdullah Gül University Affiliated: Yes


© 2020 Taylor & Francis Group, LLC.Selective leaching of a mixed nickel-cobalt hydroxide precipitate was investigated using potassium permanganate as oxidant in sulfuric acid solution. 94.9% Ni, 50% Co and 0.6% Mn were dissolved under the following conditions: sulfuric acid concentration of 0.75 M, potassium permanganate of 5 g/L, temperature of 30°C, leaching duration of 60 min, solid-to-liquid ratio of 1/10, and stirring speed of 400rpm. The pregnant leach solution was subjected to a solvent extraction process. 98% Co and 99% Mn were extracted at pH 4.84 with 30% (v/v) Cyanex 272, leaving essentially all nickel in the raffinate. Based on the experimental results, a flowsheet is proposed.