Production and mechanical characterization of prismatic shape machine element by recycling of bronze and cast-iron chips

Creative Commons License

Aslan A., Salur E., Gunes A., Sahin O. S., Karadag H. B., Akdemir A.

JOURNAL OF THE FACULTY OF ENGINEERING AND ARCHITECTURE OF GAZI UNIVERSITY, cilt.33, sa.3, ss.1013-1027, 2018 (SCI-Expanded) identifier identifier

  • Yayın Türü: Makale / Tam Makale
  • Cilt numarası: 33 Sayı: 3
  • Basım Tarihi: 2018
  • Doi Numarası: 10.17341/gazimmfd.416402
  • Dergi Adı: JOURNAL OF THE FACULTY OF ENGINEERING AND ARCHITECTURE OF GAZI UNIVERSITY
  • Derginin Tarandığı İndeksler: Science Citation Index Expanded (SCI-EXPANDED), Scopus, TR DİZİN (ULAKBİM)
  • Sayfa Sayıları: ss.1013-1027
  • Anahtar Kelimeler: Metal chips, isostatic hot pressing, metal matrix composite, recycling, mechanical characterization, ALUMINUM-ALLOY CHIPS, COMPOSITE, MICROSTRUCTURE, DEFORMATION, BEHAVIOR, PHASE
  • Abdullah Gül Üniversitesi Adresli: Hayır

Özet

In this study, the production and mechanical properties of porous metal matrix composites (MMC's) by recycling of spheroid cast iron chips (GGG-40) and bronze chips (CuSn10) by hot isostatic pressing was investigated. The metal matrix composites were produced with four different CuSn10 contents, three different pressures and temperatures and effects of production parameters on porosity, hardness, flexure properties were examined. Samples were produced in prismatic shape with specified porosity. The mechanical properties were determined by Brinell and Micro Vickers hardness tests and three-point bending test. The consolidation mechanism of metallic chips was also investigated with optic microscopy. It was examined whether any second phase occurred between metallic chips by the help of XRD test. As a result of porosity test, it is found that metal matrix composites can have porosity value of as much as 20%. It is also showed that owing to excessive plastic deformation of Cu Sn10, the hardness of MMC material can be higher than bulk CuSn10. Three-point bending test showed that the flexure properties of MMC materials are is lower than that of bulk CuSn10. As a consequence, it showed that metallic chips were recycled with hot pressing successfully.